* Steel mechanical properties and allowable stress (JIS)
| JIS 재질 (材質) |
기계적성질(機械的性質) | 기본허용응력(基本許容應力) kg/mm^2 |
|||||
| 항복내력 (降伏耐力) |
인장강도 (引張强度) |
경도(硬度) | Shaft | Gear | Material or Heat Treatment Symbol |
||
| σe | σb | HB | HS | σb/fs | σb/fc | ||
| S20C-N | >25 | >41 | 116~174 | 18~26.5 | 11.8 | 15.3 | N |
| S25C-N | >27 | >45 | 123~183 | 19.5~28 | 12.9 | 16.8 | N |
| S35C-N | >31 | >52 | 149~207 | 23~32 | 15.0 | 19.5 | N |
| S40C-N | >33 | >55 | 156~217 | 24~33 | 15.8 | 20.6 | N |
| S45C-N | >35 | >58 | 167~229 | 25.5~34 | 18.7 | 21.7 | N |
| SNC836 | >80 | >95 | 269~321 | 40~47 | 27.4 | 35.6 | SNC3,Q,T |
| SCM435 | >80 | >95 | 269~321 | 40~47 | 27.4 | 35.6 | SCM3,Q,T |
| SCM440 | >85 | >100 | 285~352 | 42~50 | 28.8 | 37.5 | SCM4,Q,T |
| SCM445 | >90 | >105 | 302~363 | 43~52 | 30.2 | 39.3 | SCM5,Q,T |
| SS400 | >22 | >41 | (118) | 18.5 | 11.8 | 15.3 | SS41 |
| SF540A | >28 | >55 | (160) | 24 | 15.8 | 20.6 | N,A |
| SC480 | >25 | >49 | (142) | 22 | 12.4 | 16.1 | |
| SC450 | >23 | >46 | (133) | 21 | 11.6 | 15.1 | |
| SCMn2A | >35 | >60 | 163~ | 25~ | 15.2 | 19.8 | N,A |
| SCMn3A | >38 | >65 | 170~ | 26~ | 16.5 | 21.4 | N,A |
| SCMn5A | >40 | >70 | 183~ | 28~ | 17.7 | 23.1 | N,A |
| FCD450 | >30 | >45 | 143~217 | 22~33 | 11.4 | 14.8 | |
| FCD600 | >40 | >60 | 185~207 | 32~42 | 15.2 | 19.8 | |
| SCMnCr3A | - | >65 | - | - | 16.5 | 21.4 | N,A |
| PBC2A | - | >20 | 60~ | - | 5.0 | 6.6 | N,A |
| Note 1. 피로한도(Fatigue Limit) : f1=2 or 2.27 (주조품(鑄造品) 2.27, 기타(其他) 2) 2. 치수효과(Size Effect) : f2= 1/0.75 (Notch가 있는 것은 별도 고려) 3. 가공(Fabricating) : f3=1.3 (Gear의 경우는 루이스(W.Lewis)식에 포함되어 있다고 생각) 4. Shaft Factor : fs=f1.f2.f3 =3.467 or 3.93 5. Gear Factor : fc=f1.f2 =2.667 or 3.02 6. 열처리 기호(Heat Treatment Symbol) N=Normalizing(불림), A=Annealing(풀림), Q=Quenching(담금질), T=Tempering(뜨임) |
|||||||