* SM35C,S35C,1035,1037,060A35,080A35,080M36,CK35,C35 Material comparison table
(carbon steel for mechanical structures)
1. Chemical composition
Code | KS | JIS | AISI | AISI | BS | BS | BS | DIN | DIN |
Material Grade |
SM35C | S35C | 1035 | 1037 | 060A35 | 080A35 | 080M36 | CK35 | C35 |
C | 0.32~0.38 | 0.32~0.38 | 0.32~0.38 | 0.32~0.38 | 0.33~0.38 | 0.33~0.38 | 0.32~0.40 | 0.32~0.39 | 0.32~0.39 |
Si | 0.15~0.35 | 0.15~0.35 | agreement | agreement | 0.10~0.40 | 0.10~0.40 | - | 0.15~0.35 | 0.15~0.35 |
Mn | 0.60~0.90 | 0.60~0.90 | 0.60~0.90 | 0.70~1.00 | 0.50~0.70 | 0.70~0.90 | 0,60~1.00 | 0.50~0.80 | 0.50~0.80 |
P | ≦0.030 | ≦0.030 | ≦0.040 | ≦0.040 | ≦0.050 | ≦0.050 | ≦0.050 | ≦0.035 | ≦0.045 |
S | ≦0.035 | ≦0.035 | ≦0.050 | ≦0.050 | ≦0.050 | ≦0.050 | ≦0.050 | ≦0.035 | ≦0.045 |
Ni | <0.20 | <0.20 | - | - | ≦0.40 | ≦0.40 | ≦0.40 | - | - |
Cr | <0.20 | <0.20 | - | - | ≦0.30 | ≦0.30 | ≦0.30 | - | - |
Mo | - | - | - | - | ≦0.15 | ≦0.15 | ≦0.15 | - | - |
Cu | <0.30 | <0.30 | - | - | - | - | - | - | - |
Remark | Ni+Cr<0.35 | Ni+Cr<0.35 | In AISI 3,5,6 C 0.31~0.38 |
- | - | - | - | - |
(Referred to KS, JIS, AISI, BS, DIN)
2. Mechanical property (SM35C,S35C)
Heat Treatment |
yield point kgf/mm^2 (N/mm^2) |
tensile strength kgf/mm^2 (N/mm^2) |
elongation % |
contraction of area % |
hardness (HB) |
charpy impact value kgf.m/cm^2 (J/cm^2) |
Normalizing 840~890℃ Air cooling |
31≦ (304)≦ |
52≦ (510)≦ |
23≦ | - | 149~207 | - |
Annealing About 830℃ Furnace cooling |
- | - | - | - | 126~163 | - |
Quenching 840~890℃ Water cooling Tempering 550~650℃ Quick cooling |
40≦ (392)≦ |
58≦ (569)≦ |
22≦ | 55≦ | 167~235 | 10≦ (98.1)≦ |
(Referred to KS, JIS)
'기술' 카테고리의 다른 글
SCM415(KS.JIS) Material comparison table (0) | 2023.12.31 |
---|---|
SCM435,4135,4137,708A37,34CrMo4 Material comparison table (2) | 2023.12.03 |
SM45C,S45C,1045,1046,080M46,CK45,C45 Material comparison table (0) | 2023.11.28 |
SCM440,4140,4142,708M40,709M40,42CrMo4 Material comparison table (0) | 2023.11.27 |
* Mechanical properties and allowable stress of mechanical materials(FEM-1987) (0) | 2022.06.09 |