* SM45C,S45C,1045,1046,080M46,CK45,C45 Material comparison table
(carbon steel for mechanical structures)
1. Chemical composition
Code | KS | JIS | AISI | AISI | BS | DIN | DIN |
Material Grade |
SM45C | S45C | 1045 | 1046 | 080M46 | CK45 | C45 |
C | 0.42~0.48 | 0.42~0.48 | 0.43~0.50 | 0.43~0.50 | 0.42~0.50 | 0.42~0.50 | 0.42~0.50 |
Si | 0.15~0.35 | 0.15~0.35 | agreement | agreement | 0.10~0.40 | 0.15~0.35 | 0.15~0.35 |
Mn | 0.60~0.90 | 0.60~0.90 | 0.60~0.90 | 0.70~1.00 | 0.60~1.00 | 0.50~0.80 | 0.50~0.80 |
P | ≦0.030 | ≦0.030 | ≦0.040 | ≦0.040 | ≦0.050 | ≦0.035 | ≦0.045 |
S | ≦0.035 | ≦0.035 | ≦0.050 | ≦0.050 | ≦0.050 | ≦0.035 | ≦0.045 |
Ni | <0.20 | <0.20 | - | - | ≦0.40 | - | - |
Cr | <0.20 | <0.20 | - | - | ≦0.30 | - | - |
Mo | - | - | - | - | ≦0.15 | - | - |
Cu | <0.30 | <0.30 | - | - | - | - | - |
Remark | Ni+Cr<0.35 | Ni+Cr<0.35 | In AISI 3,5,6 C 0.42~0.50 |
- | - | - |
(Referred to KS, JIS, AISI, BS, DIN)
2. Mechanical property (SM45C,S45C)
Heat Treatment |
yield point kgf/mm^2 (N/mm^2) |
tensile strength kgf/mm^2 (N/mm^2) |
elongation % |
contraction of area % |
hardness (HB) |
charpy impact value kgf.m/cm^2 (J/cm^2) |
Normalizing 820~870℃ Air cooling |
35≦ (343)≦ |
58≦ (569)≦ |
20≦ | - | 167~229 | - |
Annealing About 810℃ Furnace cooling |
- | - | - | - | 137~170 | - |
Quenching 820~870℃ Water cooling Tempering 550~650℃ Quick cooling |
50≦ (490)≦ |
70≦ (686)≦ |
17≦ | 45≦ | 201~269 | 8≦ (78)≦ |
(Referred to KS, JIS)